Uma Clay Test Report

Uma Clay Test Report
Product Code : Test Results
Product Description

UMA WHITE "A+" TEST REPORT

CHEMICAL ANALYSIS (As Per ED-XRF Method)

OXIDES

RESULT (%)

SiO2

48.569

Al2O3

37.202

Fe2O3

0.331

TiO2

1.114

MgO

0.116

CaO

0.137

Na2O

0.034

k2O

0.066

L.O.I. As Per ED-XRF

13.431


PHYSICAL PROPERTIES UMA WHITE "A+"

CHARACTERISTICS

UNIT

OBSERVED VALUE

VISUAL APPEARANCE

-

WHITE LUMS

RESIDUE ON # 240

%

0.50

SLAKING NATURE

-

FAST

WATER OF PLASTICITY

%

34.4

GREEN MOR

Kg/cm2

3.22    forming sp.press. : 420 Kg/cm2

DRY MOR

Kg/cm2

6.72    forming sp.press. : 420 Kg/cm2

FIRED MOR Temp At 1210 ‘C

Kg/cm2

26.61   forming sp.press. : 420 Kg/cm2

FIRED SHRINKAGE Temp At 1210 ‘C

%

3.96     cycle60 MIN.

FIRED COLOUR

-

L*93.84 A*0.68 B* 2.98 W = 84.6

W. A. Temp At 1210 ‘C

%

19.45

WORKABLE ELECTROLYTE

%

N.A.

VISCOSITY (FORD CUP : B-4Q)

(s)

N.A.

DENSITY

(g/c.c.)

N.A.

T.D.S.

ppm

150       (20% aquous soln.)

ph

-

8.45      (20% aquous soln.)

 

UMA VITRIFIED "A" TEST REPORT

 

CHEMICAL ANALYSIS (As Per ED-XRF Method)

 

OXIDES

RESULT (%)

SiO2

48.559

Al2O3

35.837

Fe2O3

0.384

TiO2

1.153

MgO

0.158

CaO

0.252

Na2O

0.016

k2O

0.092

L.O.I. As Per ED-XRF

13.470

 

PHYSICAL PROPERTIES UMA VITRIFIED "A"

CHARACTERISTICS

UNIT

OBSERVED VALUE

VISUAL APPEARANCE

-

L.PINK LUMS

RESIDUE ON # 240

%

0.80

SLAKING NATURE

-

FAST

WATER OF PLASTICITY

%

35.2

GREEN MOR

Kg/cm2

3.86   forming sp.press. : 420 Kg/cm2

DRY MOR

Kg/cm2

8.35   forming sp.press. : 420 Kg/cm2

FIRED MOR Temp At 1210 ‘C

Kg/cm2

32.95  forming sp.press. : 420 Kg/cm2

FIRED SHRINKAGE Temp At 1210 ‘C

%

4.60     cycle60 MIN.

FIRED COLOUR

-

L*92.09 A*0.84 B* 3.27 W = 83.1

W. A. Temp At 1210 ‘C

%

17.68

WORKABLE ELECTROLYTE

%

N.A.

VISCOSITY (FORD CUP : B-4Q)

(s)

N.A.

DENSITY

(g/c.c.)

N.A.

T.D.S.

ppm

170    (20% aquous soln.)

ph

-

8.44   (20% aquous soln.)

 

UMA SANITARYWARE "B+" TEST REPORT

CHEMICAL ANALYSIS (As Per ED-XRF Method)

OXIDES

RESULT (%)

SiO2

48.559

Al2O3

35.212

Fe2O3

0.463

TiO2

1.140

MgO

0.142

CaO

0.248

Na2O

0.018

k2O

0.094

L.O.I. As Per ED-XRF

13.211



 

PHYSICAL PROPERTIES UMA SANITARYWARE "B+"

CHARACTERISTICS

UNIT

OBSERVED VALUE

VISUAL APPEARANCE

-

L>PINK LUMS

RESIDUE ON # 240

%

1.1

SLAKING NATURE

-

FAST

WATER OF PLASTICITY

%

36.2

GREEN MOR

Kg/cm2

3.72    forming sp.press. : 420 Kg/cm2

DRY MOR

Kg/cm2

7.92    forming sp.press. : 420 Kg/cm2

FIRED MOR Temp At 1210 ‘C

Kg/cm2

31.80  forming sp.press. : 420 Kg/cm2

FIRED SHRINKAGE Temp At 1210 ‘C

%

4.25    cycle60 MIN.

FIRED COLOUR

-

L*90.02 A*0.12 B* 3.90 W = 82.1

W. A. Temp At 1210 ‘C

%

16.60

WORKABLE ELECTROLYTE

%

N.A.

VISCOSITY (FORD CUP : B-4Q)

(s)

N.A.

DENSITY

(g/c.c.)

N.A.

T.D.S.

ppm

170     (20% aquous soln.)

ph

-

8.84    (20% aquous soln.)

 